Fasteners - Tightening performance - Torque/Angle simplified test method

This European standard specifies a test method for fasteners with ISO metric thread from M6 to M16 and with property classes 8.8 to 12.9 for bolts and screws and with property classes 8 to 12 for nuts, to check their tightening performance in the elastic range.
It applies to steel fasteners with an ISO metric thread according to ISO 68-1.
It applies to fasteners having a friction coefficient from 0,06 up to and including 0,18. For higher values of friction coefficients, the dispersion of test results increases and the test method should not be applied. For lower values friction of coefficients, which are for very specific applications and require special lubrication, this standard does not apply.
This comparative test method can be used to monitor stability of a production process (such as coating, lubrication, shot-blasting) or to compare various production manufacturing lots. It can also be used to detect fasteners, which are out of specification.
NOTE   This simplified test method has been developed to avoid systematic use of more complex procedures.
In case of dispute the torque/tension test method according to EN ISO 16047 is the referee test.
This standard does not apply for assessment of fasteners in actual assembly conditions; it does not allow the measurement of operating friction coefficients.

Verbindungselemente - Anziehverhalten - Vereinfachtes Drehmoment/Drehwinkel-Verfahren

Dieses Dokument legt ein Prüfverfahren für Verbindungselemente mit metrischem ISO-Gewinde von M6 bis M16 für Schrauben der Festigkeitsklassen 8.8 bis 12.9 und für Muttern der Festigkeitsklassen 8 bis 12 zur Prüfung ihres Anziehverhaltens im elastischen Bereich fest.
Es gilt für Verbindungselemente aus Stahl mit metrischem ISO-Gewinde nach ISO 68-1.
Es gilt für Verbindungselemente mit einer Reibungszahl von 0,06 bis einschließlich 0,18. Bei höheren Reibungszahlwerten nimmt die Streuung der Prüfergebnisse zu und das Prüfverfahren sollte nicht angewendet werden. Dieses Dokument gilt nicht für niedrigere Reibungszahlen, die für sehr spezifische Anwendungsfälle vorgesehen sind und die eine besondere Schmierung erfordern.
Dieses vergleichende Prüfverfahren kann zur Überprüfung der Gleichmäßigkeit eines Fertigungsprozesses (z. B. Aufbringen eines Überzuges, Schmierung, Kugelstrahlen) oder zum Vergleichen von unterschiedlichen Herstellungslosen angewendet werden. Es kann auch zum Erkennen von Verbindungselementen eingesetzt werden, die nicht den Festlegungen entsprechen.
ANMERKUNG   Dieses vereinfachte Prüfverfahren wurde entwickelt, um die systematische Anwendung von umfangreicheren Verfahren zu vermeiden.
Im Streitfall dient der Drehmoment/Vorspannkraft-Versuch nach EN ISO 16047 als Schiedsprüfung.
Dieses Dokument ist nicht anwendbar für die Bewertung von Verbindungselementen im tatsächlichen Montagezustand; die Messung der im Betrieb auftretenden Reibungszahlen ist nicht möglich.

Eléments de fixation - Aptitude au serrage - Méthode d'essai simplifiée Couple/Angle

La présente Norme européenne spécifie une méthode d'essai applicable aux éléments de fixation a filetage
métrique ISO, de diametres M6 a M16, de classes de qualité 8.8 a 12.9 pour les vis et de classes de qualité 8
a 12 pour les écrous, permettant de vérifier leur aptitude au serrage dans le domaine élastique.
Elle s'applique aux éléments de fixation en acier a filetage métrique ISO conforme a l'ISO 68-1.
Elle s'applique aux éléments de fixation ayant un coefficient de frottement de 0,06 a 0,18 inclus. Pour des
coefficients de frottement supérieurs, la dispersion des résultats d'essai est plus importante et il convient de
ne pas appliquer cette méthode d'essai. La présente norme ne s'applique pas pour des coefficients de
frottement inférieurs qui correspondent a des applications tres spécifiques et nécessitent une lubrification
spéciale.
La présente méthode d'essai comparative peut etre utilisée pour contrôler la stabilité d'un procédé de
production (tel que l'application d'un revetement, la lubrification, le grenaillage) ou pour comparer différents
lots fabriqués. Elle peut également etre utilisée pour détecter des éléments de fixation en dehors des
spécifications prévues.
NOTE La présente méthode d'essai simplifiée a été élaborée afin d?éviter l'utilisation systématique de procédures
plus complexes.
En cas de litige, la méthode d'essai de couple/tension conforme au prEN ISO 16047 constitue l'essai de
référence.
La présente norme ne s'applique pas pour l'évaluation d?éléments de fixation dans des conditions
d'assemblage réelles ; elle ne permet pas de mesurer les coefficients de frottement réels.

Vezni elementi – Karakteristika privijanja - Poenostavljen preskus navora/zasuka

General Information

Status
Published
Publication Date
30-Jun-2005
Technical Committee
Current Stage
6060 - National Implementation/Publication (Adopted Project)
Start Date
01-Jul-2005
Due Date
01-Jul-2005
Completion Date
01-Jul-2005

Buy Standard

Standard
EN 14831:2005
English language
23 pages
sale 10% off
Preview
sale 10% off
Preview
e-Library read for
1 day

Standards Content (Sample)

SLOVENSKI STANDARD
SIST EN 14831:2005
01-julij-2005
Vezni elementi – Karakteristika privijanja - Poenostavljen preskus navora/zasuka
Fasteners - Tightening performance - Torque/Angle simplified test method
Verbindungselemente - Anziehverhalten - Vereinfachtes Drehmoment/Drehwinkel-
Verfahren
Eléments de fixation - Aptitude au serrage - Méthode d'essai simplifiée Couple/Angle
Ta slovenski standard je istoveten z: EN 14831:2005
ICS:
21.060.01 Vezni elementi na splošno Fasteners in general
SIST EN 14831:2005 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

---------------------- Page: 1 ----------------------

SIST EN 14831:2005

---------------------- Page: 2 ----------------------

SIST EN 14831:2005
EUROPEAN STANDARD
EN 14831
NORME EUROPÉENNE
EUROPÄISCHE NORM
April 2005
ICS 21.060.10; 21.060.20
English version
Fasteners - Tightening performance - Torque/Angle simplified
test method
Eléments de fixation - Aptitude au serrage - Méthode Verbindungselemente - Anziehverhalten - Vereinfachtes
d'essai simplifiée Couple/Angle Drehmoment/Drehwinkel-Verfahren
This European Standard was approved by CEN on 3 March 2005.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the Central Secretariat or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official
versions.
CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,
Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia,
Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36  B-1050 Brussels
© 2005 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN 14831:2005: E
worldwide for CEN national Members.

---------------------- Page: 3 ----------------------

SIST EN 14831:2005
EN 14831:2005 (E)
Contents page
Foreword.3
1 Scope .4
2 Normative references .4
3 Terms and definitions .4
4 Symbols and units.5
5 Test principle.6
6 Apparatus .6
6.1 Test device .6
6.2 Test fixture.7
6.3 Reference fasteners .10
6.4 Fasteners to be tested.11
7 Test procedure.11
7.1 General.11
7.2 Test procedure for nut testing.11
7.3 Test procedure for bolt/screw testing .12
8 Evaluation of the results .13
9 Test report .13
Annex A (normative) Calibration method for determination of the angle θθθθ .14
test
Annex B (normative) Determination of the control limit values for the torque (T and T ).17
min max
Annex C (informative) Example of determination of the control limit values for the torque (T
min
and T ).21
max
Bibliography .23

2

---------------------- Page: 4 ----------------------

SIST EN 14831:2005
EN 14831:2005 (E)
Foreword
This document (EN 14831:2005) has been prepared by Technical Committee CEN/TC 185, “Threaded and
non-threaded mechanical fasteners and accessories”, the secretariat of which is held by DIN.
This European Standard shall be given the status of a national standard, either by publication of an identical
text or by endorsement, at the latest by October 2005, and conflicting national standards shall be withdrawn at
the latest by October 2005.
This document includes a Bibliography.
According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Cyprus, Czech Republic,
Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania,
Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland
and United Kingdom.
3

---------------------- Page: 5 ----------------------

SIST EN 14831:2005
EN 14831:2005 (E)
1 Scope
This document specifies a test method for fasteners with ISO metric thread from M6 to M16 and with property
classes 8.8 to 12.9 for bolts and screws and with property classes 8 to 12 for nuts, to check their tightening
performance in the elastic range.
It applies to steel fasteners with an ISO metric thread according to ISO 68-1.
It applies to fasteners having a friction coefficient from 0,06 up to and including 0,18. For higher values of
friction coefficients, the dispersion of test results increases and the test method should not be applied. For
lower values friction of coefficients, which are for very specific applications and require special lubrication, this
document does not apply.
This comparative test method can be used to monitor stability of a production process (such as coating,
lubrication, shot-blasting) or to compare various production manufacturing lots. It can also be used to detect
fasteners, which are out of specification.
NOTE This simplified test method has been developed to avoid systematic use of more complex procedures.
In case of dispute the torque/tension test method according to EN ISO 16047 is the referee test.
This document does not apply for assessment of fasteners in actual assembly conditions; it does not allow the
measurement of operating friction coefficients.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
EN 20898-2, Mechanical properties of fasteners — Part 2: Nuts with specified proof load values — Coarse
thread (ISO 898-2:1992).
EN ISO 898-1, Mechanical properties of fasteners made of carbon steel and alloy steel — Part 1: Bolts,
screws and studs (ISO 898-1:1999).
EN ISO 4759-3, Tolerances for fasteners — Part 3: Plain washers for bolts, screws and nuts — Product
grades A and C (ISO 4759-3:2000).
EN ISO 7093-1, Plain washers — Large series — Part 1: Product grade A (ISO 7093-1:2000).
EN ISO 16047, Fasteners — Torque/clamp force testing (ISO 16047:2005).
ISO 965-2, ISO general purpose metric screw threads — Tolerances — Part 2: Limits of sizes for general
purpose external and internal screw threads — Medium quality.
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
3.1
manufacturing lot
quantity of fasteners of a single designation including product grade, property class and size, manufactured
from bar, wire, rod or flat product from a single cast, processed through the same or similar steps at the same
time or over a continuous time period through the same heat treatment and/or coating process, if any
NOTE 1 Same heat treatment or coating process means:
4

---------------------- Page: 6 ----------------------

SIST EN 14831:2005
EN 14831:2005 (E)
 for a continuous process, the same treatment cycle without any setting modification;
 for a discontinuous process, the same treatment cycle for identical consecutive loads (batches).
NOTE 2 The manufacturing lot may be split into a number of manufacturing batches for processing purposes and then
reassembled into the same manufacturing lot.
[Adapted from EN ISO 15330:1999]
3.2
coating process cycle
a sequence of surface preparation and/or coating application during a period of time where operating
parameters including temperature, concentration, surface area, current density, or any other parameter which
may affect the mechanical and/or performance properties of the fasteners are set and maintained
3.3
heat treatment cycle
a sequence of heat treatment over a defined period of time where operating parameters such as temperature,
atmosphere, pressure, retention time, or any other parameter which may affect the mechanical or
performance properties of the fasteners are set and maintained
4 Symbols and units
d Nominal diameter of the bolt, screw or nut, mm
d External diameter of the bearing part, mm
e
d Diameter of the clearance hole (block or bearing part/washer, mm)
h
d Outside diameter of the bearing face of the bolt, screw or nut, mm
w
D Diameter of bearing surface under nut or bolt head for friction (see EN ISO 16047)
b
d Basic pitch diameter, mm
2
F Force
F Clamping force corresponding to T in correlation with µ , N
p, max p min
F Clamping force corresponding to T in correlation with µ , N
p, min p max
F Clamping force corresponding to T , N
p
p
F Maximum clamping force, N
test, max
F Minimum clamping force, N
test, min
F Nominal clamping force, N
test
H Height of the tightening block, mm
h Thickness of the bearing part, mm
L Side dimension of the tightening block, mm
L Clamping length, mm
c
n Number of tested bolts, screws or nuts.
P Pitch of the thread, mm
r Mean effective radius of the bearing face, mm
m
T Torque
T Mean torque for calibration, Nm
T Maximum torque value, Nm
max
5

---------------------- Page: 7 ----------------------

SIST EN 14831:2005
EN 14831:2005 (E)
T Minimum torque value, Nm
min
T Pretorque, Nm
p
T Torque corresponding to F , Nm
test test
θ Angle of rotation
θ Angle value measured between T and T in degrees
test p test
µ Upper limit of the specified range of friction coefficient
max
µ Lower limit of the specified range of friction coefficient
min
5 Test principle
The principle of this test is to apply a specified clamping force to the bolt/screw by rotating the fastener
(bolt/screw or nut) to be tested under reference conditions.
After applying a pretorque the fastener to be tested is tightened to a specified test angle.
The final torque is monitored and compared to a specified torque range.
6 Apparatus
6.1 Test device
The torque wrench shall be able to apply a tightening torque within the uncertainty of ± 2 % of the value to be
measured. The uncertainty of angle measurement shall be ± 2 ° or ± 2 % of the measured value, whichever is
greater.
6

---------------------- Page: 8 ----------------------

SIST EN 14831:2005
EN 14831:2005 (E)
6.2 Test fixture
6.2.1 General
The test fixture includes a tightening block and a bearing part, see Figure 1.

a) Nut testing b) Bolt/screw testing
Key
1 Tightening block
2 Bearing part
3 Nut to be tested
4 Reference bolt/screw
5 Bolt/screw to be tested
6 Reference nut
Figure 1 — Test fixture
The reference fastener and the bearing part/washer shall not rotate during the test. Any device used to
prevent rotation shall not intrude into the bearing face of the fastener to be tested.
6.2.2 Tightening block
The tightening block shall be made of steel quenched and tempered to a hardness equal to or above 50 HRC.
It shall be dry and clean.
The bearing surface shall be uncoated.
7

---------------------- Page: 9 ----------------------

SIST EN 14831:2005
EN 14831:2005 (E)
Dimensions of the tightening block see Figure 2 and Table 1.
Dimensions in millimetres

Figure 2 — Tightening block
8

---------------------- Page: 10 ----------------------

SIST EN 14831:2005
EN 14831:2005 (E)
Table 1 — Dimensions of tightening block
Dimensions in milimetres
Thread of the
fastener to be
M6 M8 M10 M12 M14 M16
tested
d
L 50 ± 0,5
min.  6,40  8,40 10,50 13,00 15,00 17,00
d
h
max.  6,55  8,55 10,65 13,18 15,18 17,18
H for
nom
25 25 35 35 50 50
testing nuts
H for
nom
screws (fully  9,00 12,00 15,00 18,00 21,00 24,00
threaded)
l H for bolts (partially threaded)
nom
 30
20
 35
 40
30 25
 45
25
 50 25
35 35
 55
35 35
 60 45
45
 38
 65
45 45  38
 70 50
 80 60 60  50  50
65
 90  65  60
 65
100  78 78
 78
110  85
 85
120  95
 95
130
100
140   110
150
120
160

9

---------------------- Page: 11 ----------------------

SIST EN 14831:2005
EN 14831:2005 (E)
6.2.3 Bearing part/washer
The bearing part/washer shall be taken from a single manufacturing lot. They shall be free of burrs, uncoated,
dry and clean. The hardness of the bearing part shall be 200 HV minimum and the hardness class of the
washe
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.